A study of Nd2Fe14B and a neodymium-rich phase in sintered NdFeB magnets

The microstructure and properties of NdFeB sintered permanent magnets were analysed by different methods. Samples analysed were sintered and thermally treated. The hard magnetic Nd₂Fe₁₄B phase and amorphous neodymium-rich phase were observed by TEM. The neodymium-rich phase contained iron and boron, in elemental and in B₂O₃ form, which is known as a glass former. At the sintering temperature, Nd₂Fe₁₄B and the neodymium-rich phase are supersaturated with iron, which should be dissolved at the annealing temperature to react with neodymium and boron and form additional Nd₂Fe₁₄B phase. Iron precipitates of size up to 2 nm were detected in the Nd₂Fe₁₄B phase. These superparamagnetic precipitates of -Fe could affect the hard magnetic properties of NdFeB magnets.