Study on properties of BaxSmyTi7O20 ceramics with CaO-SiO2-B2O3 glass

The effect of CaO-SiO₂-B₂O₃ (CSB) glass addition on the sintering temperature and dielectric properties of Ba_xSm_yTi₇O₂₀ ceramics has been investigated using X-ray diffraction, scanning electron microscopy and differential thermal analysis. The CSB glass starts to melt at about 970 °C, and a small amount of CSB glass addition to Ba_xSm_yTi₇O₂₀ ceramics can greatly decrease the sintering temperature from about 1350 to about 1260 °C, which is attributed to the formation of liquid phase. It is found that the dielectric properties of Ba_xSm_yTi₇O₂₀ ceramics are dependent on the amount of CSB glass and the microstructures of sintered samples. The product with 5 wt% CSB glass sintered at 1260 °C is optimal in these samples based on the microstructure and the properties of sintering product, when the major phases of this material are BaSm₂Ti₄O₁₂ and BaTi₄O₉. The material possesses excellent dielectric properties: ?_r = 61, tan δ = 1.5 × 10⁻⁴ at 10 GHz, temperature coefficient of dielectric constant is −75 × 10⁻⁶ °C⁻¹.