Non-isothermal crystallization kinetics of MgO–BaO–B2O3–Al2O3–SiO2 glass

5MgO–9BaO–33B₂O₃–33Al₂O₃–20SiO₂ (mol%) glass was prepared by the melt quenching method at 1823 K for 2 h. Dilatometry and differential scanning calorimetry (DSC) curves of the glass have been investigated. Fragility index F was used to estimate glass formability. The crystallization kinetics of the glass was described by the activation energy (E) for crystallization and numerical factors (n, m) depending on the nucleation process and growth morphology. XRD and SEM analysis were also used to describe the crystals’ types and morphology precipitated from the MgO–BaO–B₂O₃–Al₂O₃–SiO₂ glass. The results show that the effective activation energy of the crystallization process E was 45.19 kJ/mol, and n up to 4.05. Two crystals phases, i.e. Al₄B₂O₉ and Al₂₀B₄O₃₆ were observed in the crystallized samples. SEM results were consistent with crystallization kinetics.