Phase composition and properties of solid solutions of GdFeO3–GdInO3 bulks

Solid solutions of the GdFeO₃–GdInO₃ system were prepared at 1550 °C by ceramic powder processing. The formulated composition was Gd(Fe_1−xIn_x)O₃ (GFI) with the indium contents at x = 0, 0.25, 0.5, 0.75, and 1.0. A stable phase of Gd(Fe_1/3In_2/3)O₃ in our system was identified by X-ray diffraction and phase composition analysis. Multi-phase morphologies were observed for GFI bulks with x = 0.5 and 0.75. Dielectric and electrical properties of the GFI bulks were investigated. The addition of 25% In³⁺ in GdFeO₃ had an obvious enhancement in polarization and led to an elevated resonance frequency. Dielectric properties of GFI bulks except GdInO₃ were strongly dependent upon the test frequency, which corresponded to the response of polarization mechanism. GdInO₃ displayed as a stable dielectric, which was frequency- and temperature-insensitive. GdInO₃ was thermally activated and became leaky until above 600 °C.