Abatement of diesel-exhaust pollutants: NOx storage and soot combustion on K/La2O3 catalysts

Potassium-loaded lanthana is a promising catalyst to be used for the simultaneous abatement of soot and NO_x, which are the main diesel-exhaust pollutants. With potassium loadings between 4.5 and 10 wt.% and calcination temperatures between 400 and 700 °C, this catalyst mixed with soot gave maximum combustion rates between 350 and 400 °C in TPO experiments, showing a good hydrothermal stability. There was no difference in activity when it was either mixed by grinding in an agate mortar or mixed by shaking in a sample bottle (tight and loose conditions, respectively). Moreover, when the K-loaded La₂O₃ is used as washcoat for a cordierite monolith, there were found no significant differences in the catalytic behaviour of the system, which implies its potentiality for practical purposes.

The influence of poisons as water and SO₂ was investigated. While water does not affect the soot combustion activity, SO₂ slightly shift the TPO peak to higher temperature. Surface basicity, which is a key factor, was analysed by measuring the interactions of the catalytic surface with CO₂ using the high frequency CO₂ pulses technique, which proved to be very sensitive, detecting minor changes by modifications in the dynamics of the CO₂ adsorption–desorption process. Water diminishes the interaction with CO₂, probably as a consequence of an adsorption competition. The SO₂ treated catalyst is equilibrated with the CO₂ atmosphere more rapidly if compared with the untreated one, also showing a lower interaction. The lower the interaction with the CO₂, the lower the activity.

Differential scanning calorimetric (DSC) results indicate that the soot combustion reaction coexists with the thermal decomposition of hydroxide and carbonate species, occurring in the same temperature range (350–460 °C). The presence of potassium increases surface basicity shifting the endothermic decomposition signal to higher temperatures.

We also found that NO₂ strongly interacts with both La₂O₃ and K/La₂O₃ solids, probably through the formation of monodentate nitrate species which are stable under He atmosphere until 490 °C. These nitrate species further react with the solid to form bulk nitrate compounds. The addition of Cobalt decreases the nitrates stability and catalyses the NO_x to N₂ reduction under a reducing atmosphere, which is a necessary step for a working NO_x catalytic trap. Preliminary studies performed in this work demonstrated the feasibility of using these catalysts to simultaneously remove NO_x and soot particles from diesel exhausts. The nitrate formation is still observed during the catalytic combustion of soot in the presence of NO_x, making our K/La₂O₃ a very interesting system for practical applications in simultaneous soot combustion and NO_x storage in diesel exhausts.