Argon plasma treatment of glass surfaces

The effect of argon plasma treatment of glass surfaces is studied by FTIR and SEM. The argon plasma on cleaned glass surfaces resulted in increased surface area due to microetching and surface rearrangement of the silicate network as indicated by the observed changes in the Si-O stretching infrared absorption. The result was a relative increase in surface hydrophilicity which could be optimized by the plasma reaction conditions. The etching action of the argon plasma on the substrate surfaces facilitated the removal of the micrometre thick sizing from the commercial fibres accompanied by little loss in tensile strength. Plasma was also used to graft selected monomers to the surface of glass fibres for enhancement of bond compatibility in a composite system. This grafting treatment was followed by an argon etching step. The argon plasma action on the coated surfaces improved the wettability further and increased the sur face area. Changes in surface chemistry that accompanied the argon etching treatment were very subtle in the case of the plasma polymer of allylamine, but proved significant in the case of the plasma polymer of hexamethyldisiloxane. On the latter surfaces, rearrangement of the siloxane (Si-O-Si) bonds to silylmethylene (Si-(CH₂) _n -Si) groups is suggested.