Temperature‐dependent Hall‐effect measurements of p‐type multicrystalline compensated solar grade silicon
Authors:Chiara Modanese,Maurizio Acciarri,Simona Binetti,Anne‐Karin Sø  iland,Marisa Di Sabatino,Lars Arnberg
Abstract:
In this study, we have investigated the Hall majority carrier mobility of p‐type, compensated multicrystalline solar grade silicon (SoG‐Si) wafers for solar cells in the temperature range 70–373 K. At low temperature (~70 K) the difference in the mobilities measured for the compensated and the uncompensated reference samples is the highest, and the measured mobility shows dependence on the compensation ratio. Mobilities decrease with increasing temperature, and towards room temperature, the mobilities of the different samples are in the same range. The measurements show that, for these samples, the contribution from lattice scattering is dominating over ionized impurity scattering at room temperature. In the range of interest for silicon solar cells (above room temperature), the trend in carrier mobility is similar for all the samples, and the measured value for the sample with low compensation ratio and low doping density is comparable to the uncompensated references. A comparison of resistivity and majority carrier density measured by the Hall setup at room temperature and by four‐point probe and glow discharge mass spectroscopy, respectively, is reported as well. Copyright © 2012 John Wiley & Sons, Ltd.
Keywords:multicrystalline silicon  compensation  carrier mobility  Hall effect  majority carrier density
设为首页 | 免责声明 | 关于勤云 | 加入收藏

Copyright©北京勤云科技发展有限公司  京ICP备09084417号