| Abstract: | The effect of enamel coating on long-term isothermal oxidation at 700 ℃ and cyclic oxidation at 800 ℃ in air and hot corrosion resistance of Ti-24Al-17Nb-0. 5Mo in 75% (Na2SO4 K2SO4 ) 25% NaCl (mass fraction) molten mixed salts at 700 ℃ was investigated. The results indicate that Ti-24Al-17Nb-0.5Mo alloy exhibits relatively poor long-term oxidation resistance due to the formation of Al2O3 TiO2 Nb2O5 mixed scales and poor hot corrosion resistance due to the spallation of scales formed in molten (Ns, K)2 SO4 NaCl. Enamel coating can effectively protect Ti-24Al-17Nb-0.5Mo alloy from long-term oxidation at high temperature in air and remarkably improve the hot corrosion resistance of Ti-24Al-17Nb-0. 5Mo alloy, and can act as the barrier to suppress the migration of oxygen and corrosive ions into the substrate. |