Highly Reactive β-Dicalcium Silicate: III, Hydration Behavior at 40–80°C

The effect of curing temperature (40°, 60°, 80°C) on the hydration behavior of β-dicalcium silicate (β-C₂S) was investigated. The β-C₂S was obtained by decomposition of hillebrandite, Ca₂(SiO₃)(OH)₂, at 600°C, has a specific surface area of about 7 m²/g, and is in the form of fibrous crystals. The dependence of the hydration reaction on temperature continues until the reaction is completed. The hydration is completed in 1 day at 80°C and in 14 days at 14°C. The hydration mechanism is different above and below 60°C, but at a given temperature, the reaction mechanism and the silicate anion structures of C-S-H do not change significantly from the initial to the late stages of the reaction. High curing temperature and long curing times after completion of reaction promote silicate polymerization. The Ca/Si ratio of C-S-H shows high values, being almost 2.0 above 60°C and 1.95 below 40°C.