仲钨酸铵还原制备超粗球形钨粉

以钨酸铵溶液为原料,加入含Li、Na和K碱金属盐的添加剂,在湿氢条件下还原制备粗晶球形钨粉.研究了碱金属盐的种类、含量及还原时间对仲钨酸铵粉末及钨粉的影响.通过扫描电镜、能谱仪、X射线衍射仪和检验分析筛对仲钨酸铵及粗晶钨粉的形貌、成分、物相组成及粒度分布进行表征.研究表明,采用钨酸铵溶液为原料,添加剂（NaCl、KCl和Li₂CO₃）为3 g·L-1,在1000℃湿氢条件下还原180 min,可直接制备出流动性良好、近球形、晶粒发育完整且均匀的粗晶钨粉.其平均粒径达到67μm,最大粒径可达150μm,最大松装密度为13.41 g·cm-3,最佳流动性为每50 g粗晶钨粉用时9 s. 

Preparation of coarse and spherical tungsten powders by ammonium paratungstate

Coarse and spherical tungsten powders were prepared by wet hydrogen reduction.Ammonium tungstate solutions with the additives of Li,Na and K alkali metal salts were used as raw materials.The effects of the type and content of the alkali metal salts as well as reduction time on the microstructure,chemical composition,phase composition, and particle size of ammonium paratungstate(APT) and coarse tungsten powders were investigated by scanning electronic microscopy,energy dispersive spectroscopy,X-ray diffraction,and test sieves.It is shown that ideal tungsten powders with good fluidity,sphericity,integrity and even distribution can be obtained by using the ammonium tungstate solution with 3 g·L-1 NaCl,KCl and Li₂CO₃ and reducing at 1000℃for 180 min in wet hydrogen atmosphere.The average particle size of the obtained tungsten powders is 67μm,the maximum particle size is 150μm,the biggest loose density is 13.41 g·cm-3,and the best powder flowability is 9 s for 50 g tungsten powders.