| Abstract: | This paper further illustrates the applicability of multiple internal reflectance infrared spectroscopy to the analysis of near-surface photooxidation. The results are compared with transmission infrared spectra to evaluate compositional gradients resulting from photooxidation and the influence of oxygen diffusion. The sample was a solvent-cast film of atactic, narrow distribution polystyrene, Mw of 100,000, that had been drawn to a ratio of 3.0 at 110°C by solid state coextrusion. Irradiation of these thin films, ～25μm thickness, was performed on exposure to air at 35°C for periods of up to 6 h using a mercury source emitting at 254 nm. On photooxidation, a board peak appears at 3200–3500 cm?1, attributable to hydroperoxide formation. The most dramatic increase in the infrared spectra is found for a carbonyl band at 1730 cm?1. It appears to result from an aromatic acid group since it is shifted to 1660 cm?1 on immersion of the oxidized polystyrene films in aqueous ammonium hydroxide. It is confirmed that the photooxidation of polystyrene occurs preferentially at the surface and that this reaction rate is greatly reduced in the drawn polystyrene film. |