Studies on synthetic polymer plates with high surface energy. III. Diethylene glycol bis(allyl carbonate)–unsaturated sulfonic acid system

Synthetic polymer plates (GPs) with high surface energy were prepared by the two-step copolymerization process previously reported, using diethylene glycol bis(allyl carbonate) (CR-39) as M₁ monomer and unsaturated sulfonates sodium vinyl sulfonate (VS^?Na⁺), potassium styrene sulfonate (StS^?K⁺), and sodium 2-sulfoethyl methacrylate (SEM^?Na⁺)] as M₂ monomer. The contact angle (θ_H) of water for the acid-treated (immersed in an aqueous 0.1 N HCl solution for 2 h) GPs decreased in the order StS^?K⁺, VS^?Na⁺, and SEM^?Na⁺. In the case of M₂ = SEM^?Na⁺, the θ_H value was about 20°. By adding NaCl in the immersion solution and changing the pH of the immersion solution, the θ_H values for the CR-39–SEM^?Na⁺ GPs were lowered to 18.9 and 13.1°, respectively. The θ_H values for the above GPs were smaller than those for the CR-39–acrylic acid or the CR-39–methacrylic acid GPs in the previous report, whereas the contact angle (θ_Na) of water for the former after alkali treatment (immersed in an aqueous 0.1 N NaOH solution for 2h) was larger than those for the latter. The former had durability of water wettability superior to the latter because of the difference in dissociation characteristic of the respective functional group.