NO reduction by CH4 in the presence of O2 over La2O3 supported on Al2O3

Dispersing La₂O₃ on δ- or γ-Al₂O₃ significantly enhances the rate of NO reduction by CH₄ in 1% O₂, compared to unsupported La₂O₃. Typically, no bend-over in activity occurs between 500° and 700°C, and the rate at 700°C is 60% higher than that with a Co/ZSM-5 catalyst. The final activity was dependent upon the La₂O₃ precursor used, the pretreatment, and the La₂O₃ loading. The most active family of catalysts consisted of La₂O₃ on γ-Al₂O₃ prepared with lanthanum acetate and calcined at 750°C for 10 h. A maximum in rate (mol/s/g) and specific activity (mol/s/m²) occurred between the addition of one and two theoretical monolayers of La₂O₃ on the γ-Al₂O₃ surface. The best catalyst, 40% La₂O₃/γ-Al₂O₃, had a turnover frequency at 700°C of 0.05 s^?1, based on NO chemisorption at 25°C, which was 15 times higher than that for Co/ZSM-5. These La₂O₃/Al₂O₃ catalysts exhibited stable activity under high conversion conditions as well as high CH₄ selectivity (CH₄ + NO vs. CH₄ + O₂). The addition of Sr to a 20% La₂O₃/γ-Al₂O₃ sample increased activity, and a maximum rate enhancement of 45% was obtained at a SrO loading of 5%. In contrast, addition of SO⁼₄ to the latter Sr-promoted La₂O₃/Al₂O₃ catalyst decreased activity although sulfate increased the activity of Sr-promoted La₂O₃. Dispersing La₂O₃ on SiO₂ produced catalysts with extremely low specific activities, and rates were even lower than with pure La₂O₃. This is presumably due to water sensitivity and silicate formation. The La₂O₃/Al₂O₃ catalysts are anticipated to show sufficient hydrothermal stability to allow their use in certain high-temperature applications.