Zum Spannungsrißkorrosionsverhalten rekristallisierter Bleche der AlLi-Legierung 8090-T81

On the stress corrosion cracking behaviour of recrystallized 8090-T81 Sheets The stress corrosion cracking behaviour of a recrystallized sheet of the Al-Li-Cu-Mg-Zr alloy 8090-T81 was studied performing accelerated tests under constant deformation, constant load, and slow strain rate conditions. The used electrolytes were an aqueous 3.5% NaCl solution, an aqueous solution of 2% NaCl + 0.5% Na₂CrO₄ at pH = 3, and synthetic seawater according to ASTM D1141. Alternately immersed in 3.5% NaCl solution according to ASTM G44 the investigated alloy was found to be susceptible to stress corrosion cracking was not promoted by continuous immersion in aerated 3.5% NaCl solution, 3.5% NaCl solution saturated with carbon dioxide, and in acid chromate inhibited 2% NaCl solution. Using the slow strain rate technique with continuously immersed flat tensile specimens stress corrosion cracking was only observed in synthetic seawater. Under specific environmental conditions hydrogen embrittlement can occur in the investigated material.