Low temperature pressureless sintering of dense silicon nitride using BaO-Al2O3-SiO2 glass as sintering aid |
| |
| Affiliation: | 1. School of Electromechanical Engineering, Guangdong University of Technology, Guangzhou 510006, China;2. School of Chemical Engineering and Light Industry, Guangdong University of Technology, Guangzhou 510006, China;1. Department of Metallurgical and Materials Engineering, Faculty of Technology, Sakarya University, 54187, Sakarya, Turkey;2. Materials and Surface Science Institute, University of Limerick, Limerick, Ireland |
| |
| Abstract: | Dense Si3N4 ceramic with BaO-Al2O3-SiO2 low temperature glass powders as sintering aids were prepared by pressureless sintering techniques at a relatively low temperature (1550 °C). Four kinds of glass powders of compositions melting at 1120 °C, 1300 °C, 1400 °C and 1500 °C, respectively, have been introduced as sintering aids. XRD results demonstrate that the BaO-Al2O3-SiO2 glass powders reacted with BaAl2O4 and converted into hexagonal celsian, which is a high-temperature phase with melting point of 1760 °C, so being beneficial to the high temperature properties of the materials. In addition, a portion of α-Si3N4 transformed to rod like β-Si3N4 with high aspect ratio as shown by XRD and SEM analysis. The bulk density increased with the rise of the melting temperature of the BaO-Al2O3-SiO2 glass powders, the sample obtained with the BaO-Al2O3-SiO2 glass powder melting at 1500 °C reaching a maximum density of 98.8%, an high flexural strength (373 MPa) and a fracture toughness (4.8 MPa m1/2). |
| |
| Keywords: | Low temperature pressureless sintering BAS glass powders Phase transformation Mechanical properties |
| 本文献已被 ScienceDirect 等数据库收录！ |
|