Effect of core-shell reversal on the structural,magnetic and adsorptive properties of Fe2O3-GO nanocomposites

Effect of core-shell reversal on the nanocomposites of graphene oxide (GO) and ferric oxide (Fe₂O₃) was studied. Fe₂O₃@GO core-shell nanosheets were synthesized by sonication method, while the GO@Fe₂O₃ core-shell nanospheres by employing N,N′-dicyclohexylcarbodimide as the binding agent for the wrapping of GO sheets on pre-formed Fe₂O₃ nanoparticles (NPs). The phase composition, crystallinity and morphology of the nanocomposites were characterized by FT-IR, TEM, SEM-EDS, VSM, BET surface area study and XRD techniques. The saturation magnetization (M_s) was 1.25 and 0.51 emu g^?1 for GO@Fe₂O₃ and Fe₂O₃@GO respectively owing to the dependence of magnetic properties on the reversal of core-shell. BET analysis revealed the surface area of 100.32 m² g^?1 and 45.69 m² g^?1 for GO@Fe₂O₃ and Fe₂O₃@GO nanocomposites respectively. The fabricated nanocomposites were analyzed as adsorbents for the uptake of Pb (II) ions. The impact of various factors affecting adsorption process such as pH, adsorbent dose, contact time, temperature and metal ion concentration was also investigated. GO@Fe₂O₃ core-shell nanospheres showed a higher adsorption capacity for Pb (II) ions as compared to Fe₂O₃@GO core-shell nanosheet with the maximum adsorption capacities (q_m) of 303.0 and 125.0 mg g^?1 respectively. The equilibrium data was estimated by Freundlich, Langmuir, D-R and Temkin isotherm models. Thermodynamic analysis confirmed the spontaneous and exothermic nature of the adsorption process. The adsorption kinetics was significantly fitted to pseudo-second order model. The results confirmed that core-shell reversal can significantly alter the adsorptive properties of Fe₂O₃-GO nanocomposite