Properties of Ferrite-Filled Natural Rubber Composites

Nickel zinc ferrite (Ni-ZnFe₂O₄)-filled natural rubber (NR) composite was prepared at various loading of ferrite. The tensile properties included in this study were tensile strength, tensile modulus and elongation at break. The tensile strength and elongation at break of the composites increased up to 40 parts per hundred rubber (phr) of ferrite and then decreased at higher loading whereas the tensile modulus was increased gradually with increasing of ferrite loading. Scanning electron microscopy (SEM) was used to determine the wettability of filler in rubber matrix. From the observation, the increase of filler loading reduced the wettability of the filler. Thermal stability of the composites was conducted by using a thermogravimetry analyser (TGA). The incorporation of ferrite in NR composites enhanced the thermal stability of NR composites. The swelling test results indicate that the swelling percentage of the composites decreased by increasing of ferrite loading. The initial permeability, μ_i and quality factor, Q of magnetic properties of NR composites achieved maximum value at 60 phr of ferrite loading for frequency range between 5000–40,000 kHz. The maximum impedance, Z _max of the NR composites was at the highest value at 80 phr ferrite loading for frequency range between 200–800 MHz.