Preparation and Characterization of Pt/C and Pt/TiO2 Electrocatalysts by Liquid Phase Photodeposition

The preparation of carbon and titanium dioxide supported Pt catalysts through a photochemical and photocatalytic routes were investigated. The catalysts were prepared by irradiation with UV-light (365 nm) at room temperature using H₂PtCl₆ and C₁₀H₁₄O₄Pt (Pt(acac)₂) as platinum precursors. The kinetic studies revealed that H₂PtCl₆ produced metallic platinum faster than Pt(acac)₂ and also showed that the amount of platinum deposited on TiO₂ was higher than on carbon. The samples were characterized by X-ray diffraction, SEM/EDS and cyclic voltammetry. X-ray diffraction permitted to identify the crystallographic (111) and (200) planes from platinum metal on the catalysts synthesized, the intensity of peaks depends of the amount of platinum deposited. SEM/EDS test confirmed what it was found by the kinetics studies. The electrocatalytic activity was compared with a commercial Pt E-Tek catalyst (10 wt%). The electrochemical results showed that Pt/C-AA catalyst synthesized by liquid phase photo-deposition method has stability in acid media and high distribution of the actives sites on the electrode surfaces. It could be considered as a candidate for electro-catalyst for polymer electrolyte fuel cell. The Pt/TiO₂ catalysts did not present electrochemical activity.