| 控制20CrMnTiH齿轮钢顶锻表面裂纹的措施 |
| |
| 引用本文： | 杨彬. 控制20CrMnTiH齿轮钢顶锻表面裂纹的措施[J]. 中国重型装备, 2013, 0(4): 47-50 |
| |
| 作者姓名： | 杨彬 |
| |
| 作者单位： | 乌鲁木齐新疆八一钢铁股份有限公司轧钢厂棒材分厂,新疆830022 |
| |
| 摘 要： | 分析了20CrMnTiH齿轮钢顶锻表面裂纹缺陷产生的原因,结合开裂成因给出了相应的改进措施。
|
| 关 键 词： | 20CrMnTiH齿轮钢 裂纹 改进措施 |
Measures of Control 20CrMnTiH Gear Steel Surface Crack in Upset |
| |
| Yang Bin. Measures of Control 20CrMnTiH Gear Steel Surface Crack in Upset[J]. China Heavy Equipment, 2013, 0(4): 47-50 |
| |
| Authors: | Yang Bin |
| |
| Abstract: | 20CrMnTiH gear steel surface crack origin in upset has been analyzed and relevant improvement measures have been brought up regarding to crack cause. |
| |
| Keywords: | 20CrMnTiH gear steel crack improvement measure |