Abrasive wear of WC-FeAl composites

The abrasive wear behavior of tungsten-carbide iron-aluminide composite materials was investigated using a pin-on-drum wear-testing machine. Samples were prepared by uniaxially hot pressing blended powders. The wear rates of specimens containing 40 vol.% matrix of atomic composition, Fe₆₀Al₄₀, were measured and results compared with those of conventional WC-10 vol.% Co hardmetal. They were found to be comparable to those of WC-10% Co hardmetal, when abraded by 120 μm SiC papers under identical conditions. The wear resistance of WC-Fe₆₀Al₄₀ composites increased with reduction in WC-grain size and associated with increase in composite hardness. Scanning electron microscopy revealed that the wear surfaces of WC-40% Fe₆₀Al₄₀ composites and WC-Co hardmetal were similar in appearance. The higher hardness and work hardening ability of Fe₆₀Al₄₀ binder, as compared to Co metal, are believed to be responsible for the excellent abrasive wear resistance of WC composites containing iron aluminide binder.