| Characteristics of graphite felt electrode electrochemically oxidized for vanadium redox battery application |
| |
| 作者姓名： | 李晓刚 黄可龙 刘素琴 谭宁 陈立泉 |
| |
| 作者单位： | School of Chemistry and Chemical Engineering Central South University，School of Chemistry and Chemical Engineering，Central South University，School of Chemistry and Chemical Engineering，Central South University，School of Chemistry and Chemical Engineering，Central South University，School of Chemistry and Chemical Engineering，Central South University，Changsha 410083，China，Changsha 410083，China，Changsha 410083，China，Changsha 410083，China，Changsha 410083，China Institute of Physics，Chinese Academy of Sciences，Beijing 100080，China |
| |
| 基金项目： | Project（02-09-01） supported by Pangang Group Pangzhihua Iron and Steel Research Institute, China |
| |
| 摘 要： | The graphite felt was oxidized at a positive electrode potential in sulfuric acid solution.The electrochemical performance of the treated graphite felt served as electrode for vanadium redox battery was investigated with FT-IR,SEM,XPS,BET,cyclic voltammetry and testing VRB system,respectively.The results show that the molar ratio of O to C increases from 0.085 to 0.15 due to the increase of—COOH functional groups during electrochemical oxidation treatment,and the GF surface is eroded by electrochemical oxidation,resulting in the surface area increase from 0.33 m2/g to 0.49 m 2/g.The VRB with modified GF electrode exhibits excellent performance under a current density of 30 mA/cm 2 .The average current efficiency reaches 94%and average voltage efficiency reaches 85%.The improvement of electrochemical activity for the electrode is ascribed to the increase of the number of—COOH group and the special surface of GF.
|
| 关 键 词： | 石墨 电极 电化学 氧化还原作用 电池 |
| 收稿时间： | 2006-04-13 |
| 修稿时间： | 2006-09-18 |
Characteristics of graphite felt electrode electrochemically oxidized for vanadium redox battery application |
| |
| LI Xiao-gang,HUANG Ke-long,LIU Su-qin,TAN Ning,CHEN Li-quan.Characteristics of graphite felt electrode electrochemically oxidized for vanadium redox battery application[J].Transactions of Nonferrous Metals Society of China,2007,17(1):195-199. |
| |
| Authors: | LI Xiao-gang HUANG Ke-long LIU Su-qin TAN Ning CHEN Li-quan |
| |
| Affiliation: | 1. School of Chemistry and Chemical Engineering, Central South University, Changsha 410083, China;2. Institute of Physics, Chinese Academy of Sciences, Beijing 100080, China |
| |
| Abstract: | The graphite felt was oxidized at a positive electrode potential in sulfuric acid solution. The electrochemical performance of the treated graphite felt served as electrode for vanadium redox battery was investigated with FT-IR, SEM, XPS, BET, cyclic voltammetry and testing VRB system, respectively. The results show that the molar ratio of O to C increases from 0.085 to 0.15 due to the increase of-COOH functional groups during electrochemical oxidation treatment, and the GF surface is eroded by electrochemical oxidation, resulting in the surface area increase from 0.33 m^2/g to 0.49 m^2/g. The VRB with modified GF electrode exhibits excellent performance under a current density of 30 mA/cm^2. The average current efficiency reaches 94% and average voltage efficiency reaches 85%. The improvement of electrochemical activity for the electrode is ascribed to the increase of the number of -COOH group and the special surface of GF. |
| |
| Keywords: | vanadium redox battery graphite felt electrochemical oxidation |