Comparison of corrosion behaviour of zinc in NaCl and in NaOH solutions. Part I: Corrosion layer characterization |
| |
| Authors: | M. Mouanga P. Berçot J.Y. Rauch |
| |
| Affiliation: | 1. Institut UTINAM, CNRS UMR 6213, Equipe Sonochimie et Réactivité des Surfaces, Université de Franche-Comté, 16 route de Gray, 25030 Besançon Cedex, France;2. FEMTO-ST, Université de Franche-Comté, 16 route de Gray, 25030 Besançon Cedex, France |
| |
| Abstract: | The corrosion layer formed on zinc sample in 0.6 M NaCl and 0.5 M NaOH solution under ambient conditions has been investigated. The corrosion layer morphology was analyzed using scanning electron microscopy (SEM). X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS) were used to characterize the corrosion products of zinc. The thickness evolution of the corrosion layer was investigated by glow discharge optical emission spectroscopy (GDEOS). The corrosion layer formed in 0.5 M NaOH solution appeared more compact than that formed in 0.6 M NaCl solution. Zinc hydroxide chloride (Zn5(OH)8Cl2·2H2O) and zinc hydroxide carbonate (Zn5(CO3)2(OH)6) were formed on zinc surface in 0.6 M NaCl solution while in 0.5 M NaOH solution, zinc oxide (ZnO), zinc hydroxide (Zn(OH)2) and zinc hydroxide carbonate (Zn5(OH)6(CO3)2·H2O) were detected. Probable mechanisms of zinc corrosion products formation are presented. |
| |
| Keywords: | |
| 本文献已被 ScienceDirect 等数据库收录！ |
|