Development of a new wear resistant coating by arc spraying of a steel-based cored wire |
| |
| Authors: | Lidong Zhao Binyou Fu Dingyong He and Pia Kutschmann |
| |
| Affiliation: | (1) Surface Engineering Institute, RWTH Aachen University, Juelicher Str. 334a, Aachen, Germany;(2) College of Materials Science and Engineering, Beijing University of Technology, Beijing, 100124, China |
| |
| Abstract: | In the present study, a cored wire of 304 L stainless steel as sheath material and NiB and WC-12Co as filler materials was
designed and deposited to produce a new wear resistant coating containing amorphous phase by arc spraying. The microstructure
of the coating was investigated. The porosity and hardness of the coating were determined. The wear performance of the coating
was evaluated. The XRD and TEM analyses showed that there are high volume of amorphous phase and very fine crystalline grains
in the coating. DTA measurements revealed that the crystallization of the amorphous phase occurred at 579.2°C. Because metallurgical
processes for single droplets were non-homogenous during spraying, the lamellae in the coating have different hardness values,
which lie between about 700 and 1250 HV100 g. The abrasive wear test showed that the new Fe-based coating was very wear resistant. |
| |
| Keywords: | amorphous phase arc spraying microstructure wear cored wire |