Characterization and formation mechanism of nanocrystalline (Fe,Ti)3Al intermetallic compound prepared by mechanical alloying

The nanocrystalline (Fe,Ti)₃Al intermetallic compound was synthesized by mechanical alloying (MA) of elemental powder with composition Fe₅₀Al₂₅Ti₂₅. The structural changes of powder particles during mechanical alloying were studied by X-ray diffractometry and microhardness measurements. Morphology and cross-sectional microstructure of powder particles were characterized by scanning electron microscopy. It was found that a Fe/Al/Ti layered structure was formed at the early stages of milling followed by the formation of Fe(Ti,Al) solid solution. This structure transformed to (Fe,Ti)₃Al intermetallic compound at longer milling times. Upon heat treatment of (Fe,Ti)₃Al phase the degree of DO₃ ordering was increased. The (Fe,Ti)₃Al compound exhibited high microhardness value of about 1050 Hv.