Grain boundary diffusion and segregation of Ni in Cu

Grain boundary (GB) diffusion of ⁶³Ni in polycrystalline Cu was investigated by the radiotracer technique in an extended temperature interval from 476 to 1156 K. The independent measurements in Harrison’s C and B kinetic regimes resulted in direct data of the GB diffusivity D_gb and of the so-called triple product P = s · δ · D_gb (s and δ are the segregation factor and the diffusional GB width, respectively). Arrhenius-type temperature dependencies for both the D_gb and P values were measured, resulting in the pre-exponential factors $D_{\mathrm{gb}}^0=6.93\times {10}^{-7}$ m² s⁻¹ and P₀ = 1.89 × 10⁻¹⁶ m³ s⁻¹ and the activation enthalpies of 90.4 and 73.8 kJ mol⁻¹, respectively. Although Ni is completely soluble in Cu, it reveals a distinct but still moderate ability to segregate copper GBs with a segregation enthalpy of about −17 kJ mol⁻¹.