Reflow and burn-in of a Sn-20In-0.8Cu ball grid array package with a Au/Ni/Cu pad

The intermetallic compounds formed after reflow and burn-in testing of a Sn-20In-0.8Cu solder ball grid array (BGA) package are investigated. Along with the formation of the Cu₆(Sn_0.78In_0.22)₅ precipitates (IM1) in the solder matrix, scallop-shaped intermetallic compounds (IM2) with a compositional mixture of Cu₆(Sn_0.87In_0.13)₅ and Ni₃(Sn_0.87In_0.13)₄ appear at the interfaces between the solder balls and Au/Ni/Cu pads. A significant number of intermetallic particles (IM3), with a composition of (Au_0.80Cu_0.20)(In_0.33Sn_0.67)₂, can also be found in the solder matrix. After aging at 115°C for 750 h, an additional intermetallic compound layer (IM4) with a composition of (Ni_0.91Cu_0.09)₃(Sn_0.77In_0.23)₂ is formed at the interface between IM2 and the Ni layer. The ball shear strength of the Sn-20In-0.8Cu BGA solder after reflow is 4.5 N and will rise to maximum values after aging at 75°C and 115°C for 100 h. With a further increase of the aging time at both temperatures, the joint strengths exhibit a tendency to decline linearly at about 1.7×10⁻³ N/h.