Improvement of yield strength of LM24 alloy

In this study, Al₂O₃ particles were employed to improve the microstructure of LM24 and therefore, to increase the yield strength and tensile strength of this kind of alloy. In situ Al₂O₃ particles were obtained by direct reaction between oxygen and Al melt at 750–800 °C. Microstructure examination shows that the size of in situ formed Al₂O₃ particles was about 1–2 μm, and interestingly, with addition of in situ Al₂O₃ particles, the coarse primary Si phase was disappeared completely. More important, the yield strength and the tensile strength of Al₂O₃/LM24 are increased by 52 MPa, 16 MPa than that of LM24 alloy with 0.1% Sb addition. The value of 181 MPa and 315 MPa is for yield strength and tensile strength of Al₂O₃/LM24 respectively. Besides, the yield strength and tensile strength are 180 MPa and 314 MPa respectively for Al₂O₃/LM24 alloy after remelting and casting. This verifies that the improvement of mechanical properties of such kind of material possesses stability and reliability.