| 压应力处理修复加氢反应器应力腐蚀裂纹的工程应用 | |
| 引用本文： | 陈怀宁,廖季辉. 压应力处理修复加氢反应器应力腐蚀裂纹的工程应用[J]. 石油化工腐蚀与防护, 1998, 15(4): 46-49 |
| 作者姓名： | 陈怀宁 廖季辉 |
| 作者单位： | 中国科学院金属研究所!辽宁省沈阳市110015(陈怀宁，林泉洪，陈亮山，龙昕)，扬子石化公司化工厂!江苏省南京市210048(廖季辉，李陵钢) |
| 摘 要： | 文章详细介绍了在国内外首次采用逆焊接温差处理制造压应力新工艺,以及成功修复加氢反应器产生的应力腐蚀裂纹的过程.通过这个典型事例,为国内各类化工容器或管道的防止应力腐蚀开裂提供了一条新途径. |
| 关 键 词： | 压应力处理 应力腐蚀裂纹 打磨 焊接 |
Application of Pressure Stress Treatment in Repairing Stress Corrosion Cracking of Hydrocracking Reactor |
|
| Chen Huaining,Liao Jihui,Lin Quanhong. Application of Pressure Stress Treatment in Repairing Stress Corrosion Cracking of Hydrocracking Reactor[J]. Petrochemical Corrosion and Protection, 1998, 15(4): 46-49 | |
| Authors: | Chen Huaining Liao Jihui Lin Quanhong |
| Abstract: | The new process of producing pressure stress by counter welding temperature difference treatment and its first successful application in China in repairing stress corrosion cracking of hydroprocessing reactor were detailed. This provided a new approach to prevent SCC of various vessels and pipelines in chemical production service. |
| Keywords: | pressure stress treatment stress corrosion cracking grinding welding |