The equilibrium partitioning of titanium between Ti3+ and Ti4+ valency states in CaO-SiO2-TiO x slags

The redox behavior of titanium in CaO-SiO₂-TiO _x melts was investigated using a slag-gas equilibrium technique. Titanium partitioning between Ti³⁺ and Ti⁴⁺ valency states and the ratio of activity coefficients of TiO_1.5 and TiO₂ were determined as functions of oxygen partial pressure, temperature, and slag composition. The equilibrium experiments were carried out at temperatures between 1783 and 1903 K under CO-CO₂-Ar gas atmosphere with oxygen partial pressure ranging from 10⁻¹² to 10⁻⁷ atm (1.01×10⁻¹⁰ kPa to 1.01×10⁻⁵ kPa). The slags had CaO/SiO₂ ratios between 0.55 and 1.35 and total titanium oxide concentrations from 7 to 50 mass pct. Experimental results showed that the Ti³⁺/Ti⁴⁺ ratio in CaO-SiO₂-TiO _x slags, containing up to 50 mass pct TiO _x , increased with decreasing oxygen partial pressure and decreased with increasing CaO/SiO₂ ratio and decreasing temperature. Measured variation of the redox ratio Ti³⁺/Ti⁴⁺ with oxygen partial pressure closely followed the ideal behavior. Increasing the CaO/SiO₂ ratio increased the ratio of activity coefficients of TiO_1.5 and TiO₂. The effect of total titania content on this ratio was more complex and in accord with Raman spectroscopy data.