| 连铸坯微裂纹对钢管质量的影响 |
| |
| 引用本文： | 张才安,莫礼隆.连铸坯微裂纹对钢管质量的影响[J].钢管,1992(2):39-44. |
| |
| 作者姓名： | 张才安 莫礼隆 |
| |
| 作者单位： | 重庆大学,成都无缝钢管厂,成都无缝钢管厂,成都无缝钢管厂 |
| |
| 摘 要： | 研究了连铸坯微裂纹在二辊斜轧穿孔和二辊冷轧过程中的变化。实验表明,微裂纹不能焊合,只能扩大;连铸坯的纵裂和中心裂纹导致钢管内折和外折缺陷;连铸坯横裂冷变形后衍变成人字形裂纹。
|
| 关 键 词： | 水平连铸管坯 斜轧穿孔 冷轧 微裂纹 变化 |
EFFECTS OF SLIGHT CC BILLET CRACKS ON STEEL PIPE QUALITY |
| |
| Zhang Caian.EFFECTS OF SLIGHT CC BILLET CRACKS ON STEEL PIPE QUALITY[J].Steel Pipe,1992(2):39-44. |
| |
| Authors: | Zhang Caian |
| |
| Affiliation: | Zhang Caian(Chongqing University) Mo Lilong Liu Jiazhong(Chengdu Seamless Steel Tube Plant) |
| |
| Abstract: | The developing of slight CC billet cracks during two-roll cross piercing and two-roll cold-rolling are investigated. Experiments shows that the slight cracks can not be welded but enlarges, that the longitudinal and central cracks of a CC billet lead to internal and external steel pipe wreckages, and that the transverse cracks during cold-forming develop into "herringbone" cracks. |
| |
| Keywords: | HCC billet cross-piercing cold-rolling slight cracks developing |