| 硫磺反应炉衬里失效原因分析 |
| |
| 引用本文： | 郑新兵,何宇蓉.硫磺反应炉衬里失效原因分析[J].化工设备与管道,2011,48(3):17-19,52. |
| |
| 作者姓名： | 郑新兵 何宇蓉 |
| |
| 作者单位： | 1. 中国石油大庆石化分公司炼油厂,黑龙江,大庆,163711
2. 中国石油大庆石化分公司化工一厂,黑龙江,大庆,163714 |
| |
| 摘 要： | 针对硫磺回收反应炉在生产运行过程中因衬里失效脱落，造成炉壁烧穿，从设计、施工、保护、操作等方面分析了衬里失效的原因。结合衬里失效原因，确定了衬里修复方案，做好施工质量控制和烘炉，保证了衬里修复质量。
|
| 关 键 词： | 硫磺回收 反应炉 衬里 失效 |
Cause Analysis of Failure Occurred in Lining in Sulfur Reaction Furnace |
| |
| ZHENG Xin-bing,HE Yu-rong.Cause Analysis of Failure Occurred in Lining in Sulfur Reaction Furnace[J].Process Equipment & Piping,2011,48(3):17-19,52. |
| |
| Authors: | ZHENG Xin-bing HE Yu-rong |
| |
| Affiliation: | ZHENG Xin-bing1,HE Yu-rong2(1.Refinery of Daqing Petrochemical Branch,CNPC,Daqing 163711,China,2.First Chemical Factory of Daqing Petrochemical Branch,Daqing 163714,China) |
| |
| Abstract: | In production process,the shell of sulfa recovery furnace was burned and perforated because the inner lining was fall off.With respect to this accident,the failure cause was analyzed in this article from the aspects of design,fabrication,protection and operation.From the analysis result,the lining repair scheme was determined.The lining repair quality was,then,guaranteed. |
| |
| Keywords: | sulfa recovery reaction furnace lining failure |