Synthesis and Properties of MoSi2–MoB–SiC Ceramics

MoB and SiC particulate reinforced MoSi₂ matrix composites were synthesized in situ from Mo, Si, and B₄C powder mixtures by self‐propagating high‐temperature synthesis (SHS). The SHS MoSi₂–MoB–SiC products were vacuum hot‐pressed (HPed) at 1400°C for 90 min to fabricate high‐density (> 97.5% relative density) bulk composites. Microstructure refinement and improvements in the Vickers hardness and fracture toughness of the HPed composites were observed with increasing B₄C content in the reaction mixture. The HPed composite of composition MoSi₂–0.4MoB–0.1SiC exhibited grain size of 1–5 μm, Vickers hardness of 12.5 GPa, bending strength of 537 MPa, and fracture toughness of 3.8 MPa.m^1/2. These excellent mechanical properties indicate that MoB and SiC particulate reinforced MoSi₂ composites could be promising candidates for structural applications.