| 微波原位聚合PLA纳米复合材料的结构与性能 | |
| 引用本文： | 袁维波,王鹏,曹海雷,雷海芬.微波原位聚合PLA纳米复合材料的结构与性能[J].合成树脂及塑料,2008,25(3):61-64. |
| 作者姓名： | 袁维波 王鹏 曹海雷 雷海芬 |
| 作者单位： | 1. 哈尔滨工业大学市政环境工程学院绿色化学与技术研究中心,黑龙江,哈尔滨,150090;凯莱英医药化学(天津)有限公司,天津,300457 2. 哈尔滨工业大学市政环境工程学院绿色化学与技术研究中心,黑龙江,哈尔滨,150090 3. 凯莱英医药化学(天津)有限公司,天津,300457 |
| 基金项目： | 黑龙江省哈尔滨市科技攻关项目 |
| 摘 要： | 将D,L-丙交酯和有机蒙脱土(OMMT)在连续微波辐照下开环聚合,合成聚乳酸(PLA)/有机蒙脱土(OMMT)纳米复合材料.对复合材料的力学性能及热性能测试表明,在PLA中加入w(0MMT)为0.1%时,其拉伸强度和断裂伸长率均达到最佳,相对于纯PLA分别提高了60.75%和7.85%;PLA的热失重中心温度提高了8℃,即提高了复合材料的热稳定性.分析复合材料的X射线衍射谱图、透射电子显微镜和扫描电子显微镜照片表明:OMMT主要以剥离状态分散在PLA基体中,形成以剥离型为主、同时存在插层结构的纳米复合材料,OMMT的加入使复合材料的拉伸断面由脆性断裂向韧性断裂转变. |
| 关 键 词： | 聚乳酸 有机蒙脱土 纳米复合材料 微波辐照 原位聚合 |
Structure and properties of polylactide nano-composite polymerized in situ under microwave irradiation |
|
| Yuan Weibo,Wang Peng,Cao Hailei,Lei Haifen.Structure and properties of polylactide nano-composite polymerized in situ under microwave irradiation[J].China Synthetic Resin and Plastics,2008,25(3):61-64. | |
| Authors: | Yuan Weibo Wang Peng Cao Hailei Lei Haifen |
| Affiliation: | Yuan Weibo~(1,2) Wang Peng~1 Cao Hailei~1 Lei Haifen~2 (1. Research Center for Green Chemistry , Technology,School of Municipal , Environmental Engineering,Harbin Institute of Technology,Harbin 150090,China,2. Asymchem Laboratories (Tianjin) Co.,Ltd,Tianjin 300457,China) |
| Abstract: | Polylactic acid/organo-montmorillonite (PLA/OMMT) nano-composite was synthesized in bulk via ring opening polymerization in situ of D,L-lactide in the presence of organo-montmorillonite under continuous microwave irradiation. The analyses of mechanical properties reveal that when dosage of OMMT is 1% by mass fraction the tensile strength and the elongation at break of the nano-composite reach its optimum values, increased by 60.75% and 7.85% respectively,compared with pure PLA. The central temperature of he... |
| Keywords: | polylactide organo-montmorillonite nano-eomposite microwave irradiation polymerization in situ |