Efficient dye-sensitized solar cells based on CNTs and Zr-doped TiO2 nanoparticles

The light scattering, harvesting and adsorption effects in dye-sensitized solar cells (DSSCs) are studied by preparation of coated carbon nanotubes (CNTs) with TiO₂ and Zr-doped TiO₂ nanoparticles in the forms of mono- and double-layer cells. X-ray diffraction (XRD) analysis reveals that the phase composition of Zr-doped TiO₂ electrode is a mixture of anatase and rutile phases with major rutile content, whereas it is the same mixture with major anatase content for coated CNTs with TiO₂. Furthermore, the average crystallite size of Zr-doped TiO₂ electrode is slightly decreased with Zr introduction. Field emission scanning electron microscope (FE-SEM) images show that the porosity of Zr-doped TiO₂ electrodes is higher than that of undoped electrode, enhancing dye adsorption. UV–visible spectroscopy analysis reveals that the absorption onset of Zr-doped TiO₂ electrodes is slightly shifted to longer wavelength (the red-shift) in comparison with that of undoped TiO₂ electrode. Moreover, the band gap energy of TiO₂ nanoparticles is decreased by Zr introduction, enhancing light absorption. It is found that electron injection of monolayer TiO₂ electrode is improved by introduction of 0.025 mol% Zr, resulted in enhancement of its power conversion efficiency (PCE) up to 6.81% compared with 6.17% for pure TiO₂ electrode. Moreover, electron transport and light scattering are enhanced by incorporation of 0.025 wt% coated CNTs with TiO₂ in the over-layer of double layer electrode. Therefore, double layer solar cell composed of 0.025 mol% Zr-doped TiO₂ nanoparticles as the under-layer and mixtures of these nanoparticles and 0.025 wt% coated CNTs with TiO₂ as the over-layer shows the highest PCE of 8.19%.