Production of primary recrystallized Si- Fe foil with orientation near (110)[001] and magnetic properties |
| |
Authors: | W Abe M Iwasaki K Kosuge Y Ushigami T Nozawa |
| |
Affiliation: | (1) Hirohata R&D Lab., Nippon Steel Corp., Himeji, Hyogo, Japan;(2) Steel Research Labs., Nippon Steel Corp., Futtu, Chiba, Japan |
| |
Abstract: | T he magnetic properties and features of magnetic domain structures of recently developed grain-oriented 15 to 50 μm thick
Si-Fe foil with very high permeability were investigated. The reported induc-tion values of these materials were 1.70 to 1.95
T at 800 A/m. These high values produced low core losses. The losses of toroidal cores made of 50-μm thick material was W15/400 = 8.0 W/kg and W18/400 = 12.5 W/kg. Despite the presence of a very small primary recrystallized grain size, they consisted of simple magnetic domains
with 180° domain walls; ac magnetization was achieved by simple 180° domain wall displacement. The cut core, made of 20μn
thick material, was W10/10k = 330 W/kg and W15/10k = 580 W/kg, which compares to those of amorphous cut cores. |
| |
Keywords: | core loss cut core foil magnetic materials Si-Fe foil |