Electrospun Pt/TiO2 hybrid nanofibers for visible-light-driven H2 evolution

One-dimensional (1D) Pt/TiO₂ hybrid nanofibers (HNFs) with different concentrations of Pt were fabricated by a facile two-step synthesis route combining an electrospinning technique and calcination process. X-ray diffraction (XRD), scanning electron microscopy (SEM), and high-resolution transmission electron microscopy (HRTEM) results showed that the Pt nanoparticles (NPs) with the size of 5–10 nm were well dispersed in the TiO₂ nanofibers (NFs). Further investigations from the UV–Vis diffuse reflectance (DR) and X-ray photoelectron spectroscopy (XPS) analysis revealed that some Pt ions were incorporated into the TiO₂ lattice as Pt⁴⁺ state, which contributed to the visible light absorption of TiO₂ NFs. Meanwhile, the Pt²⁺ ions existing on the surface of Pt NPs resulted in the formation of Pt–O–Ti bond at Pt NPs/TiO₂ NFs interfaces that might serve as an effective channel for improving the charge transfer. The as-electrospun Pt/TiO₂ HNFs exhibited remarkable activities for photocatalytic H₂ evolution under visible light irradiation in the presence of l-ascorbic acid as the sacrificial agent. In particular, the optimal HNFs containing 1.0 at% Pt showed the H₂ evolution rate of 2.91 μmol h⁻¹ and apparent quantum efficiency of 0.04% at 420 nm by using only 5 mg of photocatalysts. The higher photocatalytic activity could be ascribed to the appropriate amount of Pt ions doping and excellent electron-sink effect of Pt NPs co-catalysts.