Evolution of crystallographic alignment in Tb-Fe-B melt-spun ribbons |
| |
Authors: | LIU Rongming CHEN Jingwu DENG Yunwen NA Ran LIU Weiqiang YUE Ming ZHANG Jiuxing |
| |
Affiliation: | College of Materials Science and Engineering,Beijing University of Technology;Anhui Earth-Panda Advance Magnetic Material Co.,Ltd. |
| |
Abstract: | Ternary Tb-Fe-B ribbons were prepared via melt-spun technique under different wheel speeds of 5-25 m/s.Effect of wheel speed on the crystal structure and microstructure of the ribbons was investigated.All the ribbons quenched under different wheel speeds crystallized in single Tb2Fe14B phase with tetragon structure.Different crystallographic alignment evolutions were observed in the free side surface and wheel side surface of the ribbons.On the free-side surface,an in-plane c-axis crystal texture of Tb2Fe14B phase was found in the ribbons quenched at 5 m/s.However,with the increase in the wheel speed,the direction of the c-axis texture turns to perpendicular to the ribbon surface.On the wheel-side surface,a strong c-axis texture perpendicular to the ribbon surface was observed in the ribbons quenched at 5 m/s,and then weakened gradually with the increase in the wheel speed.Further investigation showed that the competition of the two types of temperature gradients during the quench process was responsible for the crystallographic alignment evolution in the ribbons. |
| |
Keywords: | ternary Tb-Fe-B ribbon Tb2Fe14B phase crystallographic alignment temperature gradient rare earths |
本文献已被 维普 等数据库收录! |
|