Effect of Li2O on the crystallization behavior of CaO-Al2O3-SiO2-Li2O-Ce2O3 mold slags

The effect of Li₂O on the crystallization properties of CaO-Al₂O₃-SiO₂-Li₂O-Ce₂O₃ slags was investigated. With increasing the Li₂O content, LiAlO₂ and CaCeAlO₄ were the main crystalline phases. LiAlO₂ formed for the charge compensating of Li⁺ ions to AlO₄^5?]-tetrahedrons, and CaCeAlO₄ formed as a result of the charge balance of Ce³⁺ ions, Ca²⁺ ions, and AlO₆^9?]-octahedrons. Increasing the content of Li₂O to 10%, the crystallization temperature was the highest, and the incubation time was the shortest. The crystallization ability was strong due to the three factors of strengthening the interaction between ions and ion groups, decreasing the polymerization degree, and increasing the melting temperature. Further increasing the content of Li₂O, the crystallization performance was obviously suppressed, because the melting temperature and the force between the cations and the anion groups decreased.