| 特高频高磁损耗材料的制备及其磁特性研究 |
| |
| 引用本文： | 孙宏亮,王群.特高频高磁损耗材料的制备及其磁特性研究[J].电子元件与材料,2005,24(12):14-16. |
| |
| 作者姓名： | 孙宏亮 王群 |
| |
| 作者单位： | 北京142号信箱408分箱,北京,100854;北京工业大学材料学院新型功能材料教育部重点实验室,北京,100022;北京工业大学材料学院新型功能材料教育部重点实验室,北京,100022 |
| |
| 基金项目： | 北京市自然科学基金;北京市教委科研项目 |
| |
| 摘 要： | 采用磁粉芯工艺制备了抑制电磁干扰(EMI)用高磁损耗软磁合金复合材料(SCM)。通过SEM微观形貌观察与复磁导率(μr'、μr')测试,对不同制备阶段的样品进行了分析,研究了球磨与退火过程对磁导率的影响,并与铁氧体材料磁导率特性进行了对比。结果表明:μr'呈磁共振双峰宽频分布,1.2GHz时,μr'为7.3,μr'max为14.5。特高频带内,SCM磁损耗性能超过铁氧体材料。
|
| 关 键 词： | 复合材料 软磁合金 复磁导率 磁共振双峰 铁氧体 |
| 文章编号： | 1001-2028（2005）12-0014-03 |
| 收稿时间： | 2005-07-11 |
| 修稿时间： | 2005-07-11 |
Study on Preparation of High Magnetic Losses Material in UHF Band and the Permeability Characteristics |
| |
| SUN Hong-liang,WANG Qun.Study on Preparation of High Magnetic Losses Material in UHF Band and the Permeability Characteristics[J].Electronic Components & Materials,2005,24(12):14-16. |
| |
| Authors: | SUN Hong-liang WANG Qun |
| |
| Affiliation: | 1. POB 142, Beijin, Beijing 100854, China; 2. Key Laboratory of Advanced Functional Materials, Ministry of Education, Institute of Materials Science and Engineering, Beijing University of Technology, Beijing 100022, China |
| |
| Abstract: | High magnetic losses soft magnetic alloy composites material(SCM)used for electromagnetic interference suppression was fabricated by magnetic core preparation method.SEM micromorphology observation and complex permeability(μ r',μ r')measure were used to analyze samples with different preparation periods.Influence of ball milling and annealing processes to permeability characteristics was studied.Permeability characteristics of ferrite material and SCM were compared.The results show that μ r' exhibits twin peak magnetic resonance and broad band dispersion characteristics,when frequency is 1.2 GHz,μ r'= 7.3,μ r'max=14.5.Magnetic losses performance of SCM is excellence than ferrite material in ultra high frequency band. |
| |
| Keywords: | composite materials soft magnetic alloy complex permeability twin peak of magnetic resonance ferrite |