高铁三水铝石型矿的酸浸性能

对于铝硅比低的高铁铝土矿采用拜耳法已不能经济地提取。以国外某低品位三水铝石矿为研究对象，采用盐酸为浸出介质对其进行酸浸性能研究。主要考察矿石粒度、液固比及时间和温度对浸出效果的影响。结果表明:温度对铝元素浸出效果影响显著。当矿石粒度55 μm，液固比100∶7，温度105℃，时间120 min，采用密闭加压方式浸出，此时铝元素和铁元素的浸出率均高于95%，均得到有效浸出，与浸出渣产物表征一致；对该高铁三水矿酸浸过程进行动力学研究表明，铁和铝的酸浸过程均受内扩散控制。 

Acid Leaching Performance of Gibbsite-type Bauxite with High Iron Content

High-iron bauxite with low A/S ratio cannot be extracted economically by Bayer process. Taking a low-grade gibbsite ore abroad as the research object, the acid leaching performance of gibbsite was studied by using hydrochloric acid as leaching medium. The effects of ore particle size, liquid-solid ratio, time and temperature on leaching efficiency were investigated. The results show that temperature has a significant effect on the leaching effect of aluminum. When the particle size of ore is 55 μm, the ratio of liquid to solid is 100:7, the temperature is 105℃, and the time is 120 min, the leaching rate of aluminum and iron are both higher than 95%, and they are effectively leached. It is consistent with the characterization of leaching residue. The kinetics of the acid leaching process of the high iron gibbsite ore shows that the acid leaching process of iron and aluminum is controlled by internal diffusion.