| 聚氨酯泡沫上化学镀镍研究 |
| |
| 引用本文： | 张景怀,惠志林,徐惠萍,方正秋,余成洲.聚氨酯泡沫上化学镀镍研究[J].稀有金属,2001,25(4):278-281. |
| |
| 作者姓名： | 张景怀 惠志林 徐惠萍 方正秋 余成洲 |
| |
| 作者单位： | 北京有色金属研究总院 |
| |
| 摘 要： | 实验给出了聚氨酯泡沫的粗化和化学镀镍工艺参数；研究了对化学镀镍沉积速度影响的因素，发现温度、还原剂和金属镍盐浓度是主要影响因素，随着温度的升高及还原剂与镍盐浓度的增大，镀速增加。化学镀镍后经电镀、热解和热处理制得泡沫镍。
|
| 关 键 词： | 化学镀镍 聚氨酯 泡沫镍 |
| 文章编号： | 0258-7076(2001)04-0278-04 |
| 修稿时间： | 2000年10月30 |
Study on Electroless
Nickel on Foam Polyurethane |
| |
| Zhang Jinghuai,Hui Zhilin,XU Huiping,Fang Zhengqiu,Yu Chengzhou.Study on Electroless
Nickel on Foam Polyurethane[J].Chinese Journal of Rare Metals,2001,25(4):278-281. |
| |
| Authors: | Zhang Jinghuai Hui Zhilin XU Huiping Fang Zhengqiu Yu Chengzhou |
| |
| Abstract: | The process of electroless plating nickel on the polyurethane foam was studied. It was discovered that the main factors affecting plating nickel rate are temperature,concentration of reducing agent and nickel salt. As the temperature rises and the concentration of reducing agent and nickel salt increases,plating nickel rate increases too.Nickel foam was fabricated by electroforming,pyrolyzing and annealing after electroless plating nickel. |
| |
| Keywords: | Electroless Nickel polyurethane Nickel foam |