热处理对Ti600高温钛合金组织和性能的影响 |
| |
引用本文: | 郭萍,洪权,戚运连,辛社伟.热处理对Ti600高温钛合金组织和性能的影响[J].钛工业进展,2010,27(1):22-24. |
| |
作者姓名: | 郭萍 洪权 戚运连 辛社伟 |
| |
作者单位: | 西北有色金属研究院,陕西,西安,710016 |
| |
基金项目: | 国家973计划项目,国家科技支撑计划项目 |
| |
摘 要: | 实验用Ti600合金为采用二次真空自耗电弧炉熔炼而成的600 kg铸锭,经开坯锻造后最终轧制成棒材,经金相法测定Ti600合金的相变点为tβ=1 010℃。着重分析了不同的热处理制度对Ti600合金显微组织和力学性能的影响。结果表明:获得网篮组织可使合金的综合性能匹配较好;在相变点以上进行1 020℃×2 h+AC,650℃×8 h+AC处理,可获得较好的综合性能。
|
关 键 词: | 高温合金 热处理 力学性能 显微组织 |
Effect of Heat Treatment on Microstructures and Mechanical Properties of Ti600 High Temperature Titanium Alloy |
| |
Authors: | Guo Ping Hong Quan Qi Yunlian Xin Shewei |
| |
Affiliation: | (Northwest Institute for Nonferrous Metal Research, Xi'an 710016, China) |
| |
Abstract: | The original material of Ti-600 alloy used in the present work was drawn from the 600 kg ingots, which were melted twice in a consumable electro-arc furnace, and with a diameter of 360 mm. Hot-rolled bar stock of Ti-600, 14 mm in diameter, was obtained after the breaking-down, forging and roiling craft. β transformation point detected by metallographic analysis was 1 010 ℃. The effect of heat treatment on the microstructure and mechanical properties of the alloy was mainly analyzed. The results show that basket-weave structure obtained can make the best combination property of the alloy, and the best heat treatment regimes are 1 020 ℃ × 2 h + AC and 650 ℃ × 8 h+AC. |
| |
Keywords: | high temperature titanium alloy heat treatment microstructures mechanical properties |