| 含P高强度IF钢酸轧拉矫断带分析和工艺改进 |
| |
| 引用本文： | 李俊生,薛仁杰,马娥,曹晓恩,罗翔.含P高强度IF钢酸轧拉矫断带分析和工艺改进[J].特殊钢,2019,40(2):53-56. |
| |
| 作者姓名： | 李俊生 薛仁杰 马娥 曹晓恩 罗翔 |
| |
| 作者单位： | 1河钢集团邯钢公司技术中心汽车家电板研发中心，邯郸056015；
2河钢集团钢研总院，石家庄050023 ；
3北京科技大学工程技术研究院，北京100083) |
| |
| 摘 要： | 采用化学成分、扫描电镜及俄歇电子能谱等手段分析了含P高强IF钢HC250IF酸轧拉矫断带原因,明确B含量低未能抑制P的晶界偏聚,形成的FeTiP或Fe3P化合物导致晶界脆性是酸轧拉矫断带的根本原因。通过优化加硼工艺、提高钢中B含量从0.0002%～0.0007%升至0.000 8%～0.0012%、严格控制N含量≤30×10-6、RH添加硼铁后真空净循环≥8 min保证成分均匀性的措施可有效避免含P高强IF钢酸轧拉矫断带
|
| 关 键 词： | 含P高强IF钢 断带 磷偏聚 硼 |
| 收稿时间： | 2018-10-11 |
Analysis on Strip Fracture of High Strength IF Steel Containing Phosphorus During Straightening in Pickling & Rolling and Process Improvement |
| |
| Li Junsheng,Xue Renjie,Ma E,Cao Xiaoen,Luo Xiang.Analysis on Strip Fracture of High Strength IF Steel Containing Phosphorus During Straightening in Pickling & Rolling and Process Improvement[J].Special Steel,2019,40(2):53-56. |
| |
| Authors: | Li Junsheng Xue Renjie Ma E Cao Xiaoen Luo Xiang |
| |
| Affiliation: | 1 Automotive & Appliance Sheet R & D Center, Technique Center, Handan Company, Hesteel Group, Handan 056015;
2 Technology Research Institute, Hesteel Group, Shijiazhuang 050023;
3 Beijing University of Science and Technology,Engineering Technology Research Institute,Beijing 100083 |
| |
| Abstract: | The chemical composition, scanning electron microscopy and auger electron spectroscopy were used to analyze the reasons of the strip fracture of high strength IF steel HC250IF containing phosphorus during straightening in pickling & rolling process. It is confinned that the content of B is too low and the segregation of P at grain boundary could not be inhibited,and the FeTiP or Fe3P compound formed at the grain boundary resulting in brittleness is the basic cause of strip fracture. By optimized process for adding boron, increasing the content of B from 0.0002% ?0.0007% to 0.0008% ~ 0.0012% , controlling strictly the content N≤ 30 x 10-6 and vacuum cycle for 8 min after adding the boron iron in RH process, it is to ensure the uniformity of the composition, the strip fracture of high strength IF steel containing phosphorus during straightening in pickling & rolling process can be effectively avoided. |
| |