Improvement of coercivity and thermal stability of Nd-Fe-B sintered magnets by intergranular addition of Tb80Fe20 alloy

To improve the coercivity and temperature stability of Nd-Fe-B sintered magnets for high-temperature applications, the eutectic Tb₈₀Fe₂₀ (wt%) alloy powders were added into the Nd-Fe-B sintered magnets by intergranular method to enhance the coercivity (H_cj) and thermal stability. The microstructure, magnetic properties and thermal stability of the Nd-Fe-B magnets with different Tb₈₀Fe₂₀ contents were studied. The experimental results demonstrate that the coercivity (H_cj) of the sintered Nd-Fe-B magnet is significantly enhanced from 14.12 to 27.78 kOe, and the remanence (B_r) decreases not obviously by introducing 4 wt% Tb₈₀Fe₂₀ alloy. Meanwhile, the reversible temperature coefficients of coercivity (β) and remanence (α) of the Nd-Fe-B magnets are increased from ?0.5634%/℃ to ?0.4506%/℃ and ?0.1276%/℃ to ?0.1199%/℃ at 20–170 ℃, respectively. The Curie temperature (T_C) of the Nd-Fe-B magnet is slightly enhanced with the increase of Tb₈₀Fe₂₀ content. Moreover, the irreversible flux magnetic loss (h_irr) is obviously reduced as Tb₈₀Fe₂₀ addition increases. Further analysis of the microstructure reveals that a modified microstructure, i.e. clear and continuous RE-rich grain boundary layer, is acquired in the sintered magnets by introducing Tb₈₀Fe₂₀ alloy. The associated mechanisms on improved coercivity and thermal stability were comprehensively researched.