Mechanical Properties and Microstructure of X120 Grade High Strength Pipeline Steel |
| |
Authors: | ZHANG Ji-ming SUN Wei-hua SUN Hao |
| |
Affiliation: | Technology Center,Jinan Steel and Iron Group Corporation,Jinan 250101,Shandong,China |
| |
Abstract: | A new ultrahigh strength pipeline steel with high yield strength and high impact toughness was fabricated in this work,and mechanical properties and microstructure of the steel were investigated.The steel exhibited outstanding mechanical properties with yield strength levels of up to 951 Mpa and tensile strength levels up to 1023 Mpa.The sharp notch toughness with absorbed energy values of 227J/cm2 at-30℃ and shear area of up to 95% in drop weight tear test (DWTT) at temperature of-20℃ were achieved.It was found that microstructure of the steel comprises a majority of low-carbon lath bainite with different sublaths and sub-sublaths,meanwhile there is a high density of dislocation between laths and the dispersed film-like martensite-austenite (M-A) constituents.Most of the precipitates in this steel are duplex type containing Nb and Ti with characterized morphology of cap with the range of precipitation size from a few to tens nanometers. |
| |
Keywords: | pipeline steel mechanical properties lath bainite precipitate |
本文献已被 CNKI 维普 万方数据 ScienceDirect 等数据库收录! |
| 点击此处可从《钢铁研究学报(英文版)》浏览原始摘要信息 |
|
点击此处可从《钢铁研究学报(英文版)》下载全文 |