| Effect of Black Plate on Corrosion Resistance of T5 Tinplate |
| |
| 作者姓名： | HUANG Xing-qiao LI Ning JIANG Li-min LI De-yu |
| |
| 作者单位： | Department of Applied Chemistry, Harbin Institute of Technology, Harbin 150001, Heilongjiang, China |
| |
| 摘 要： | The effect of black plate on corrosion resistance of T5 tinplate was studied by glow discharge spectrograph, X-ray diffractometer （XRD）, stress tester, roughness tester and metallographic microscope. The result shows that black plate influences corrosion resistance of T5 tinplate intensely. It also indicates that the increase of content of manganese, phosphorus, silicon and aluminum in black plate would reduce the corrosion resistance of T5 tinplate and the increase of degree of crystal orientation on （200） crystal face, ｜X-Y｜ value （internal stress difference within two orientation）, roughness and exposure degree of iron grain after the same acid wash of black plate would enhance the corrosion resistance of T5 tinplate and the grain number of black plate has small effect on corrosion resistance of T5 tinplate.
|
| 关 键 词： | 马口铁 黑钢板 晶体取向 内压 腐蚀抗力 |
| 修稿时间： | 2004-06-21 |
Effect of Black Plate on Corrosion Resistance of T5 Tinplate |
| |
| HUANG Xing-qiao LI Ning JIANG Li-min LI De-yu.Effect of Black Plate on Corrosion Resistance of T5 Tinplate[J].Journal of Iron and Steel Research,2006,13(2):59-64. |
| |
| Authors: | HUANG Xing-qiao LI Ning JIANG Li-min LI De-yu |
| |
| Affiliation: | Department of Applied Chemistry, Harbin Institute of Technology, Harbin 150001, Heilongjiang, China |
| |
| Abstract: | The effect of black plate on corrosion resistance of T5 tinplate was studied by glow discharge spectrograph,X-ray diffractometer (XRD), stress tester, roughness tester and metallographic microscope. The result shows that black plate influences corrosion resistance of T5 tinplate intensely. It also indicates that the increase of content of manganese, phosphorus, silicon and aluminum in black plate would reduce the corrosion resistance of T5 tinplate and the increase of degree of crystal orientation on (200) crystal face, |X-Y| value (internal stress difference within two orientation), roughness and exposure degree of iron grain after the same acid wash of black plate would enhance the corrosion resistance of T5 tinplate and the grain number of black plate has small effect on corrosion resistance of T5 tinplate. |
| |
| Keywords: | T5 tinplate black plate component crystal orientation internal stress corrosion resistance |