Effect of Tempering Temperature on Microstructure and Mechanical Properties of Steel Containing Ni of 9 %
Authors:ZHAO Xi-qing  PAN Tao  WANG Qing-feng  SU Hang  YANG Cai-fu  YANG Qing-xiang
Affiliation:1. State Key Laboratory of Metastable Materials Science and Technology, Yanshan University, Qinhuangdao 066004, Hebei, China
2. Division of Structural Material Research, Central Iron and Steel Research Institute,Beijing 100081, China
Abstract:Mechanical properties of quenching, intercritical quenching and tempering (QLT) treated steel containing Ni of 9% were evaluated from specimens subject to various tempering temperatures. The detailed microstructures of steel containjng Ni of 9% at different tempering temperatures were observed by optical microscope (OM) and transmission electron microscope (TEM). The volume fraction of austenite was estimated by XRD. The results show that high strength and cryogenic toughness of steel containing Ni of 9% are obtained when the tempering temperature are between 540 and 580 ℃ . The microstructure keeps the dual phase lamellar structure after the intercritical quenching and there is cementite created in the Ni-rich constituents when tempering temperature is 540 ℃. When tempering temperatures are between 560 and 580 ℃ , the reversed austenites (γ') grow up and the dual phase lamellar structure is not clear. The γ' becomes instable at 600 ℃. When tempered at temperature ranging from 500 to 520 ℃ , the increase of dislocation density in the lamellar matrix makes both tensile strength and yield strength decrease. When tempered at 540 ℃ and higher temperature, the yield strength decreases continuously because the C and alloying elements in the matrix are absorbed by the cementite and the γ', so the yield ratio is decreased by the γ'. There are two toughness mechanisms at different tempering temperatures. One is that the precipitation of cementite absorbs the carbon in the steel which plays a major role in improving cryogenic toughness at lower temperature. Another is that the γ' and the purified matrix become major role at higher tempering temperature. When the tempering temperature is 600 ℃ ,the stability of γ' is decreased quickly, even the transformation takes place at room temperature, which results in a sharp decrease of Charpy-V impact energy at 77 K. The tempering temperature range is enlarged by the special distribution of cementite and the lamellar structure.
Keywords:steel containing Ni of 9 %  tempering temperature  cementite  reversed austenite  cryogenic toughness