A novel method of strong and tough Si3N4 ceramic from the particle-stabilized foam

The brittleness of Si₃N₄ ceramics has always limited its wide application. In this paper, Si₃N₄ ceramics were prepared based on foam. Combining the unique honeycomb structure of the ceramic foams and the self-toughening mechanism of Si₃N₄, the strengthening and toughening of Si₃N₄ ceramics can be further achieved by adjusting the microstructure of Si₃N₄ ceramic foams. The powder particles are self-assembled by particle-stabilized foaming to form a foam body with a honeycomb structure. It was pretreated at different temperatures (1450–1750°C). The microstructure evolution of foamed ceramics at different pretreatment temperatures and the conversion rate of α-Si₃N₄ to β-Si₃N₄ at different pretreatment temperatures were explored. Then the foamed ceramics with different microstructures are hot-press sintered to prepare Si₃N₄ dense ceramics. The effects of different microstructures of foamed ceramics on the strength and toughness of Si₃N₄ ceramics were analyzed. The experimental results show that the relative density of Si₃N₄ ceramics prepared at a particle pretreatment temperature of 1500°C is 97.8%, and its flexural strength and fracture toughness are relatively the highest, which are 1089 ± 60 MPa and 12.9 ± 1.3 MPa m^1/2, respectively. Compared with the traditional powder hot-pressing sintering, the improvement is 21% and 33%, respectively. It is shown that this method of preparing Si₃N₄ ceramics based on foam has the potential to strengthen and toughen Si₃N₄ ceramics.