Properties and structures of nonstoichiometric (K,Na)NbO3‐based lead‐free ceramics

The 0.968(K_0.48Na_0.52)]Nb_0.95+xSb_0.05O₃–0.032(Bi_0.5Na_0.5)ZrO₃ KNN_xS–BNZ] lead‐free ceramics with nonstoichiometric niobium ion were fabricated via conventional solid‐state sintering technique and their piezoelectric, dielectric and ferroelectric properties were investigated. When x = 0.010, enhanced piezoelectric properties (d₃₃ ≈ 421 pC/N and k_p ≈ 0.47) were obtained due to the construction of rhombohendral—tetragonal phase boundary near room temperature. The KNN_xS–BNZ ceramics possesses enhanced Curie temperature (T_c) with improved piezoelectric constant. A large d₃₃ of ~421 pC/N and a high T_c ~256°C can be simultaneously induced in the ceramics with x = 0.010. Especially, good thermal stability was observed in a broad temperature range. The results indicated that our work could benefit development of KNN‐based ceramics and widen their application range.