Phase,domain, and microstructures in Sr2+ substituted low-temperature sintering PZT-based relaxor ferroelectrics

The Ag-Pd internal electrode of multilayer piezoelectric ceramics needs to be sintered below 1000°C, and lead wires and components need to be welded with lead-free solder at 260°C. PNN–PMW–PZT–xSr piezoelectric ceramics with high Curie temperature (T_c > 260°C) were synthesized at a low sintering temperature (960°C) to meet the requirements of multilayer piezoelectric devices. The relationship between structures (phase, domain, and microstructures) and electrical properties (piezo/ferroelectric properties, and dielectric relaxation) in the Sr²⁺ substituted ceramics was investigated. Rietveld refinement and Raman spectra show that Sr²⁺ substitution can cause the phase change and increase the force constant of BO₆] octahedron. The piezoelectric response increases with increasing the content of the tetragonal phase (CTP) in the rhombohedral-tetragonal (R-T) coexisted ceramics. The ceramics with 0.6 mol% Sr²⁺ substitution have minimum activation energy for domain wall movement (E_a) of 0.0362 eV which favors the formation of nanometer-sized domains, and possess excellent electrical properties (d₃₃ = 623 pC/N, d₃₃^* =783 pm/V, T_c =295°C). The higher the CTP, the lower the E_a. The lower E_a favors the rotation of polarization direction and extension, and is beneficial to the generation of the nanometer-size domains, resulting in high piezoelectric properties.